316/316L Stainless Steel Sheet Plate

Jiangsu ranboyu Stainless Steel is also the leading agent of TISCO, BAOSTEEL, LISCO, JISCO, ZPSS mills etc. Through many years of sustained knowledge, we have built close partnership with many steel manufacturers and mills to supply stainless steel products stably. Technical backup of these world's largest mills, our products are mostly used in Medical equipment, Food industry, Construction material, Kitchen utensils etc.

Inquire Now Next Product

Description

Commodity	stainless steel plate sheet
Grade	201,202,304,304L,309S,310S,316,316L,316Ti,317L,321,347H,409,409L,410,420,430,etc
Brand	TISCO ,BAO STEEL,POSCO,JISCO,LISCO
Certification	ISO,SGS,BV
Thickness	0.3mm-60mm
Width	1000mm,1219mm(4feet),1250mm,1500mm,1524mm(5feet),
Width	1800mm,2200mm or as your requirements
Length	2000mm,2440mm(8feet),2500mm,3000mm,3048mm(10feet)
Length	5800mm, 6000mm or as your requirements
Surface	NO.1, NO.2D, NO.2B, BA,NO.3, NO.4,NO.240,NO.400,Hairline,NO.8,Brushed
Standard	ASTM,AISI,SUS,JIS,EN,DIN,BS,GB,etc
Delivery time	5 days after confirming the order
MOQ	1 ton
Package	Stainless steel sheet packing:Waterproof paper + Metal Pallet or as per customers' requirements. The inner size of container is below:
	20ft GP: 5.8m(length) x 2.13m(width) x 2.18m(high) about 24-26CBM,23MTS
	4 0ft GP: 11.8m(length) x 2.13m(width) x 2.18m(high) about 54CBM,27MTS
	40ft HG: 11.8m(length) x 2.13m(width) x 2.72m(high) about 68CBM,27MTS
Payment term	L/C at sight or 30% TT as deposit and the balance paid against copy of B/L
Applications	architectural decoration, luxury doors, elevators decorating, metal tank shell, ship building, decorated inside the train, as well as outdoor works, advertising nameplate, the ceiling and cabinets, aisle panels, screen, the tunnel project, hotels, guest houses, entertainment place, kitchen equipment, light industrial and others.
Advantages	Showing the splendor of your quality, wear-resistant as well, strong corrosion resistance and decorative effect, durable and beautiful in good taste.

Heat Treatment

Type 201 is not hardenable by heat treatment.
Annealing: Anneal at 1850 – 1950 °F (1010 – 1066 °C), then water quench or rapidly air cool.
The annealing temperature should be kept as low as possible, consistent with the desired properties, because Type 201 tends to scale more than Type 301

Table 1 – Typical Mechanical Properties*

UTS ksi (MPa)	0.2% YS ksi (MPa)	Elongation % in 2" (50.8 mm)	Hardness Rockwell
110 (758)	52 (360)	55	B87

*Annealed condition

Table 2 – Impact Strength

Izod V-Notch Rockwell ft·lbs. (J)

120 (163)

Table 3 – Cold-Worked Properties*

Condition	UTS ksi (MPa) min.	0.2% YS ksi (MPa) min.	Elongation % in 2" (50.8 mm)		Elongation % in 2" (50.8 mm)
Condition	UTS ksi (MPa) min.	0.2% YS ksi (MPa) min.	< 0.015 in.	≥ 0.015 in.	Elongation % in 2" (50.8 mm)
1/4 hard	125 (862)	75 (517)	25	25	30
1/2 hard	150 (1034)	110 (150)	15	18	35
3/4 hard	175 (1207)	135 (931)	10	12	37
Full hard	185 (1276)	140 (965)	8	9	41

*Standard practice is to produce to either minimum tensile strength, minimum yield strength or minimum hardness, but not to combinations of these properties.